Fe-Ni Soft Magnetic Alloy (GBn198-1988)
Sort | Grade | Composition | International Similar Grade | |||
IEC | Russia | U.S.A. | ||||
High initial permeability of soft magnetic alloy | 1J79 | Ni79Mo4 | E11c | 79НМ | Mumeta | |
1J85 | Ni80Mo5 | E11c | 79НМА | |||
High magnetic conductivity higher saturation magnetic flux density soft magnetic alloy | 1J46 | Ni46 | E11e | 46Н | 45-Permalloy | |
1J50 | Ni50 | E11a | 50Н | Hy-Ra49 | ||
Chemical Composition:
Grade | ChemicalComposition(%) | ||||||||||
C | P | S | Mn | Si | Ni | Cr | Co | Mo | Cu | Fe | |
1J46 | ≤0.03 | ≤0.02 | ≤0.02 | 0.6-1.1 | 0.15-0.30 | 45-46.5 | - | - | - | ≤0.2 | Balance |
1J50 | ≤0.03 | ≤0.02 | ≤0.02 | 0.3-0.6 | 0.15-0.30 | 49-50.5 | - | - | - | ≤0.2 | Balance |
1J79 | ≤0.03 | ≤0.02 | ≤0.02 | 0.6-1.1 | 0.30-0.50 | 78.5-81.5 | - | - | 3.8-4.1 | ≤0.2 | Balance |
1J85 | ≤0.03 | ≤0.02 | ≤0.02 | 0.3-0.6 | 0.15-0.30 | 79-81 | - | - | 4.8-5.2 | ≤0.2 | Balance |
Mechanical Property :
Grade | Resisitivity | Desinty (g/cm3) | CuriePoint | HighSaturatedmagneto-strictioncoefficient | Brinellhardness | σbTensile | σsYieldStrength | Elongation | ||||
unan- | an- | unan- | an- | unan- | an- | unan- | an- | |||||
1J46 | 0.45 | 8.2 | 400 | 25 | 170 | 130 | 735 | 735 | 3 | |||
1J50 | 0.45 | 8.2 | 500 | 25 | 170 | 130 | 785 | 450 | 685 | 150 | 3 | 37 |
1J79 | 0.55 | 8.6 | 450 | 2 | 210 | 120 | 1030 | 560 | 980 | 150 | 3 | 50 |
1J85 | 0.56 | 8.75 | 400 | 0.5 | - | - | - | - | - | - | - | - |